Researchers drew attention three years ago when they reported that a two-dimensional perovskite – a material with a specific crystal structure – composed of cesium, lead and bromine emitted a strong green light. Crystals that produce light on the green spectrum are desirable because green light, while valuable in itself, can also be relatively easily converted to other forms that emit blue or red light, making it especially important for optical applications ranging from light-emitting devices to sensitive diagnostic tools.
But there was no agreement about how the crystal, CsPB2Br5, produced the green photoluminescence. Several theories emerged, without a definitive answer.
Now, however, researchers from the United States, Mexico and China, led by an electrical engineer from the University of Houston, have reported in the journal Advanced Materials they have used sophisticated optical and high-pressure diamond anvil cell techniques to determine not only the mechanism for the light emission but also how to replicate it.
They initially synthesized CsPB2Br5 from a related material known as CsPbBr3 and found that the root cause of the light emission is a small overgrowth of nanocrystals composed of that original material, growing along the edge of the CsPB2Br5 crystals. While CsPbBr3, the base crystal, is three-dimensional and appears green under ultraviolet light, the new material, CsPB2Br5, has a layered structure and is optically inactive.
“Now that the mechanism for emitting this light is understood, it can be replicated,” said Jiming Bao, associate professor of electrical and computer engineering at UH and corresponding author on the paper. “Both crystals have the same chemical composition, much like diamond versus graphite, but they have very different optical and electronic properties. People will be able to integrate the two materials to make better devices.”
Potential applications range from solar cells to LED lighting and other electronic devices.
Bao began working on the problem in 2016, a project that ultimately involved 19 researchers from UH and institutions in China and Mexico. At the time, there were two schools of scientific thought on the light emission from the cesium crystal: that it emitted green light due to a defect, mainly a lack of bromine, rather than the material itself, or that a variation had unintentionally been introduced, resulting in the emission.
His group started with the synthesis of a clean sample by dropping CsPbBr3 powder in water, resulting in sharper-edged crystals. The sharper edges emitted a stronger green light, Bao said.
The researchers then used an optical microscope to study the individual crystals of the compound, which Bao said allowed them to determine that although the compound is transparent, “something was going on at the edge, resulting in the photoluminescence.”
They relied on Raman spectroscopy – an optical technique that uses information about how light interacts with a material to determine the material’s lattice properties – to identify nanocrystals of the original source material, CsPbBr3, along the edges of the crystal as the source of the light.
Bao said CsPbBr3 is too unstable to use on its own, but the stability of the converted form isn’t hampered by the small amount of the original crystal.
The researchers said the new understanding of the light emission will yield new opportunities to design and fabricate novel optoelectronic devices. The techniques used to understand the cesium-lead-halide compound can also be applied to other optical materials to learn more about how they emit light, Bao said.
In addition to Bao, researchers involved with the project include: Chong Wang, Yanan Wang, Xinghua Su, Shengyu Dai, Zhaojun Qin, Francisco C. Robles-Hernandez and Yan Yao, all from the Department of Electrical and Computer Engineering at UH; Viktor G. Hadjiev of the Department of Mechanical Engineering at UH; Yizhou Ni and Shuo Chen of the UH Department of Physics; Md. Kamrul Alam of the materials science and engineering program at UH; Zhiming Wang of the University of Electronic Science and Technology of China; Guoying Feng of Sichuan University; Hector A. Calderon Benevides of the Instituto Politecnico Nacional; Haiyan Wang, Jie Jian and Qiang Li of Purdue University; and Quinkai Yu of Texas State University.